In order to improve the success rate of high temperature and complex formation structural oil wells, the preparative temperature sensitive self?consolidation resin is used to modify the surface of the aggregate material, and the thermally consolidated rigid plug material is obtained, then auxiliaries are chosen to build a novel bridge sealing and thermal consolidation plugging system that could resist temperature to 190 ℃. Infrared spectroscopy, thermal analysis, scanning electron microscopy were employed to study the molecular structure, microstructure and thermal stability of the resin, thermally consolidated rigid plug material and the plugging system, the suspension stability, consolidation rate, consolidation strength and permeability of the plugging system were also investigated. The results show that the constructed plugging system has the advantages of good suspension stability and wide solidification time window in bentonite slurry with mass fraction of 5%, and the compressive strength of the solidified body after curing at 90~190 ℃ are all over 6 MPa; at the same time, the water phase permeability of the solidified body cured at 190 ℃ is 6.32×103 μm2 under the driving pressure of 12 MPa, and the plugging rate is more than 98.00%. It is expected to meet the plugging requirements of high?temperature formation.